Thermoplastic polyesters, and method of making hollow articles therefrom

ABSTRACT

Disclosed are new copolyesters of terephthalic acid, bis(4-β-hydroxyethyoxyphenyl)sulfone, ethylene glycol and a very small amount of a trifunctional cross-linking agent, particularly useful as molding compounds, especially for the extrusion-blow molding process of making hollow articles, and a method of making hollow articles.

Poly(ethylene terephthalate) resins are excellent molding compounds for making various hollow articles such as bottles for comestibles, and the like. Poly(ethylene terephthalate) has good fatigue resistance and, therefore, its uses include applications where the product is subjected to fatigue-inducing conditions, such as molding compounds for bottles known as squeeze bottles, wherein the product can be ejected from the container by a squeeze pressure. It is known to make various containers from poly(ethylene terephthalate) by first injection molding a preform, reheating the preform to approximately blowing temperature, placing the preform in the closed halves of a blow mold and blowing the preform to the desired shape.

The good fatigue resistance of poly(ethylene terephthalate) has been attributed to its crystalline structure and its tendency to become oriented, which increases strength.

One deficiency, however, of poly(ethylene terephthalate) has been its low glass transition temperature, which prevents its use as containers for many comestibles that are hot filled.

Another particular deficiency of poly(ethylene terephthalate) is that in the molten state it is a Newtonian fluid and as a consequence has poor melt strength. The practical effect of this is that containers of poly(ethylene terephthalate) cannot be produced by the process of extruding a soft tube of poly(ethylene terephthalate) and enclosing the tube in a blow mold and completing the blowing. This is because the poly(ethylene terephthalate) at the temperature necessary for extrusion as a tube will not maintain its tubular shape while warm even long enough to enclose the tube in the blow mold, because of its Newtonian behavior and poor melt strength. Thus, poly(ethylene terephthalate) preforms or parisons for blow molding are made by injection molding.

The glass transition temperature of a polymer of terephthalic acid and ethylene glycol can be improved by replacing part of the ethylene glycol with bis(4-β-hydroxyethoxyphenyl) sulfone, but the resulting copolyester is also a nearly Newtonian fluid and has poor melt strength and, consequently, also cannot be used in the extrusion-blow molding method of making containers.

Newtonian flow is defined as the type of flow occurring in a liquid system where the rate of shear is directly proportional to the shearing force. Non-Newtonian flow is observed when the rate of shear is not directly proportional to the shearing force. Poly(ethylene terephthalate) exhibits Newtonian flow. The polyesters or copolyesters of the present invention have non-Newtonian flow and such non-Newtonian flow characteristics tend to impart melt strength to such polyesters.

I have now found that a high polymer thermoplastic copolyester resulting from polymerizing certain proportions of terephthalic acid, bis(4-β-hydroxyethoxyphenyl) sulfone (BSE), ethylene glycol (EG) and small amounts of (a) a triol of the formula RC(CH₂ OH)₃ where R is methyl or ethyl, or (b) trimesic acid (TMA) or its anhydride or its low alkyl, C₁ to C₄ esters, has good melt strength; the polymer so produced has non-Newtonian properties with a good relationship between the melt viscosity and the shear rate. Such polymers have somewhat less fatigue resistance (or folding endurance) than poly(ethylene terephthalate) but still entirely adequate for application to making squeeze bottles or other products that undergo significant flexing in use. Other desirable properties of the polymers will be discussed hereafter.

While it is believed that the desired non-Newtonian behavior of the polymer melt, obtained by use of one of the above trifunctional additives, is because of cross linking of the polymer molecules, it has been found that the effect of such cross linking on folding endurance of fatigue resistance is really not predictable. Thus, while the use of pentaerythritol, instead of one of the present additives, also increases the melt strength and creates the non-Newtonian property of the melt of such copolyesters, its use also nearly completely destroys the fatigue resistance or folding endurance of the resulting polymer.

It is an object of the invention to provide new thermoplastic polyesters having improved rheological properties combined with good physical properties.

It is another object of the invention to provide a new process for making hollow articles of ethylene terephthalate polyesters having a desirable combination of properties.

Other objects, as well as aspects and advantages of the invention, will become apparent from the accompanying disclosure and discussion.

According to one aspect of the present invention, there is provided a thermoplastic copolyester consisting essentially of the polymeric reaction product of

(A) reactant(s) selected from terephthalic acid and its C₁ to C₄ alkyl esters, and

(B) reactants, bis(4-β-hydroxyethoxyphenyl) sulfone and ethylene glycol, and

(C) reactant(s) selected from (a) a triol of the formula RC(CH₂ OH)₃ where R is methyl or ethyl, and (b) trimesic acid, its anhydride, and its C₁ to C₄ alkyl esters,

wherein the amount of said bis(4-β-hydroxethoxphenyl) sulfone is 2-25, usually 2-20, mol percent of the amount of A reactants, the combined amount of B reactants is about 110 to 300 mol percent of the amount of A reactants, and the amount of C reactant(s) is 0.1 to 0.7 mol percent of the amount of said A reactants, said copolyester having oxygen (O₂) and CO₂ permeabilities in cc.mil/100 in².day.atm. of less than 9 and less than 62, respectively, a glass transition temperature, Tg, of at least 82° on an unoriented basis, said copolyester further having non-Newtonian flow properties. When more of the C reactant is employed, the folding endurance begins to decrease excessively; moreover, the melt strength becomes so high that molding thereof is to all intents and purposes not practicably possible if much over 0.7 mol percent is used.

According to a further aspect of the invention, I have provided a new method for making hollow articles. Thus, in the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more diols by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said blow mold walls, I have provided the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of my invention as defined hereinabove.

As before noted, the use of carefully selected amounts of the trifunctional additive (C reactant) enables the making of hollow articles by extruding a tubular preform and, while still hot and soft, enclosing said preform in a blow mold and blowing same. I have also discovered that the inclusion of the BSE component serves, among other things, to lower the melting point of the polymer and thus allows a lower extrusion temperature to be used than is the case with PET. BSE also lowers the rate of crystallization and thus makes it less prone to premature crystallization in producing the hollow preform. This in turn helps minimize thermal and oxidative degradation problems to which polyesters made from ethylene terephthalate are prone at working temperatures above the polyester melting point, Tm.

In the following illustrative examples and in the claims, the oxygen and the carbon dioxide permeabilities refer to the determinations made on substantially unoriented pressed films.

The glass transition temperature, Tg, and the melting point were determined using a Perkin-Elmer differential scanning calorimeter, Model DSC-2, in a manner similar to that described in U.S. Pat. No. 3,822,332 issued July 2, 1974, using a heating rate of 10° C./minute.

FIG. 1 plots the apparent melt viscosity in poises versus shear rate. Such curves are explained in Severs, Rheology of Polymers, Rheinhold, New York, 1962, pp. 25 et seq. Apparent viscosity is the ratio of the shear stress over shear rate. Curve C is for "pure" poly(ethylene terephthalate) (PET) which is an essentially Newtonian fluid having completely unsatisfactory melt strength. Curve B is for the three component copolyester of Example 1, having no trifunctional additive, and is little better than PET. The data was obtained using an Instron Capillary Rheometer using a melt temperature of 270° C. Curve A is typical of a copolyester of the invention and is non-Newtonian.

The inherent viscosities were measured at 25° C., using a solution of 0.25 gms. of polymer dissolved in 100 milliliters of a mixture of 3 weight parts phenol with 2 weight parts 1,1,2,2-tetrachloro-ethane. All polymers of the invention have inherent viscosities of over 0.6 measured in this manner.

Examples 2, 3, 4, 5, 6 and 7 are examples of copolyesters within the scope of the invention and each has the combination of properties set forth hereinbefore for copolyester compositions of the invention.

EXAMPLE 1

Copolyester prepared from dimethyl terephthalate, ethylene glycol and bis(4-β-hydroxyethoxyphenyl) sulfone.

291.3 g of dimethyl terephthalate, 233.4 g of ethylene glycol and 0.0919 g of Mn(OAc) ₂.4H₂ O were charged into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser. The reaction mixture was heated to 190° C. for 2 hours, 210° C. for 2 hours under nitrogen atmosphere. Methanol was continuously distilled out during this period. Then 76.1 g of bis (4-β-hydroxyethoxyphenyl) sulfone, 0.1093 g of Sb₂ O₃, 0.255 g of (PhO)₃ P (i.e., triphenyl phosphite) and 0.0894 g of tetrakis [2,4-di-tertiarybutylylphenyl] 4,4' biphenylenediphosphonite were added into the reactor. The reaction temperature was raised to 260° C. and maintained for 45 minutes. The nitrogen gas flow was turned off and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. for 41/4 hours. The inherent viscosity of the copolyester was 0.77. The polymer melt did not show adequate melt strength and was nearly Newtonian as shown in FIG. 1. A pressed film of about 10 mil thick required 48 times of cyclic foldings before losing its tear strength completely. The copolyester had a Tg of 98° C., oxygen permeability of 8.2 cc.mil/100 in².day atm and a carbon dioxide permeability of 56.8 cc.mil/100 in².day.atm. The melting point was 215° C.

EXAMPLE 2 (0.2 mole percent trimethyl-1,3,5-benzenetricarboxylate)

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser, the following were added:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis (4-beta-hydroxyethoxyphenyl) sulfone

0.7567 g of trimethyl-1,3,5-benzenetricarboxylate

0.0919 g of Mn(OAc)₂.4H₂ O

0.1093 g of Sb₂ O₃

The reaction mixture was heated at 200° C. for 13/4 hours under nitrogen atmosphere. Methanol was continuously distilled out during this period. Then 0.225 g of triphenyl phosphite was added to the mixture in the reactor.

The reaction temperature was increased to 260° C. under nitrogen atmosphere. After 10 minutes, at 260° C., the nitrogen gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. under such vacuum for 3 hours. The copolyester had an inherent viscosity of 0.79. The polymer melt showed good melt strength. A pressed film about 10 mil thick required 22 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 96° C. The oxygen gas permeability was 8.6 cc.mil/100 in².day.atm.

EXAMPLE 3 (0.7 mole percent trimethyl-1,3,5-benzenetricarboxylate)

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser, the following were added:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis (4-beta-hydroxyethoxyphenyl) sulfone

2.6483 g of trimethyl 1,3,5 benzenetricarboxylate

0.0919 g of Mn(OAc)₂.4H₂ O

0.1093 g of Sb₂ O₃

The reaction mixture was heated to 197° C. for 1 hour and 45 minutes under nitrogen atmosphere. Methanol was continuously distilled out during this period. Then 0.225 g of triphenyl phosphite was added to the mixture in the reactor.

The reaction temperature was increased to 260° C. under nitrogen atmosphere. After 10 minutes at 260° C., the nitrogen gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. under such vacuum for 3 hours. The copolyester had an inherent viscosity of 0.99. The polymer melt showed very good melt strength. A pressed film of about 10 mil thick required 17 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 96° C. The oxygen gas permeability was 8.1 cc.mil/100 in².day.atm.

EXAMPLE 4 (0.2 mole percent 2-ethyl-2-(hydroxymethyl) 1,3-propanediol)

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser, the following were added:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76,1 g of bis(4-beta-hydroxyethoxyphenyl) sulfone

0.4025 g of 2-ethyl-2-(hydroxymethyl)-1,3 propanediol

0.0919 g of Mn(OAc)₂.4H₂ O

0.1093 g of Sb₂ O₃.

The reaction mixture was heated at 197° C. for 13/4 hours under nitrogen atmosphere. Methanol was continuously distilled out during this period. Then 0.225 g of triphenyl phosphite was added to the mixture in the reactor.

The reaction temperature was increased to 260° C. under nitrogen atmosphere. After 10 minutes at 260° C., the nitrogen gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. under such vacuum for 3 hours. The copolyester had an inherent viscosity of 0.76. The polymer melt showed good melt strength. A pressed film of about 10 mil thick required 32 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 97° C.

EXAMPLE 5 (0.7 mole percent 2-ethyl-2-(hydroxymethyl)-1,3-propanediol)

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser, the following were added:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis(4-beta-hydroxyethoxyphenyl) sulfone

1.408 g of 2-ethyl-2-(hydroxymethyl)-1,3-propanediol

0.0919 g of Mn(OAc)₂.4H₂ O

0.1093 g of Sb₂ O₃

The reaction mixture was heated at 197° C. for 13/4 hours under nitrogen atmosphere. Methanol was continuously distilled during this period. Then 0.225 g of triphenyl phosphite was added to the mixture in the reactor.

The reaction temperature was increased to 260° C. under nitrogen atmosphere. After 10 minutes at 260° C., the nitrogen gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. under such vacuum for 3 hours. The copolyester had an inherent viscosity of 0.71. The polymer melt showed very good melt strength. A pressed film of about 10 mil thick required 16 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 96° C.

EXAMPLE 6 (0.2 mole percent 2-methyl-2-(hydroxymethyl)-1,3-propanediol)

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port and a condenser, the following were added:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis(4-beta-hydroxyethoxyphenyl) sulfone

0.3604 g of 2-methyl-2-(hydroxymethyl)-1,3-propanediol

0.0919 g of Mn(OAc)₂ -4H₂ O

0.1093 g of Sb₂ O₃

The reaction mixture were heated at 197° C. for 13/4 hours under nitrogen atmosphere. Methanol was continuously distilled out during this period. The 0.225 g of triphenyl phosphite was added to the mixture in the reactor.

The reaction temperature was increased to 260° C. under nitrogen atmosphere. After 10 minutes at 260° C., the nitrogen gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 275° C. under such vacuum for 3 hours. The copolyester had an inherent viscosity of 0.81. The polymer melt showed good melt strength. A pressed film of about 10 mil thick required 44 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 96° C.

EXAMPLE 7 (0.7 mole percent 2-methyl-2-(hydroxymethyl) 1,3-propanediol)

The ester interchange reaction and polycondensation reaction was carried out as in Example 6 with the following feed composition:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis(4-beta-hydroxyethoxyphenyl) sulfone

1.2616 g of 2-methyl-2-(hydroxymethyl)-1,3-propanediol

0.0919 g of Mn(OAc)₂ -4H₂ O

0.1093 g of Sb₂ O₃

0.225 g of triphenyl phosphite was added after the ester interchange reaction

The copolyester had an inherent viscosity of 0.83. The polymer melt showed very good melt strength. A pressed film of about 10 mil thick required 18 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 96° C. The oxygen gas permeability was 8.6 cc.mil/100 in².day.atm.

EXAMPLE 8 (0.8 mole percent 2-methyl-2-(hydroxymethyl)-1,3-propanediol)

The ester interchange reaction and polycondensation reaction was carried out as in Example 6 with the following feed composition:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis(4-β-hydroxyethoxyphenyl) sulfone

1.4418 g of 2-methyl-2-(hydroxymethyl)-1,3-propanediol

0.0919 g of Mn(OAc)₂ -4H₂ O

0.1093 g of Sb₂ O₃

0.225 g of triphenyl phosphite was added after the ester interchange reaction

The copolyester had an inherent viscosity of 0.78. A pressed film of about 10 mil thick required only 12 cyclic foldings before losing its tear strength. The DSC glass transition was 96° C. The oxygen gas permeability was 8.4 cc.mil/100 in.².day.atm.

EXAMPLE 9 (0.8 mole percent trimethyl 1,3,5 benzentricarboxylate)

The ester interchange reaction and polycondensation reaction was carried out as in Example 6 with the following feed composition:

291.3 g of dimethyl terephthalate

233.4 g of ethylene glycol

76.1 g of bis(4-β-hydroxyethoxyphenyl) sulfone

3.0266 g of trimethyl-1,3,5-benzenetricarboxylate

0.0919 g of Mn (OAc)₂ -4H₂ O

0.1093 g of Sb₂ O₃

0.225 g of triphenyl phosphite was added after the ester interchange reaction

The reaction time at 275° C. under less than 0.4 mm Hg vacuum was 2 hours and 35 minutes. The copolyester had an inherent viscosity of 0.79. The polymer melt showed very good melt strength. A pressed film of about 10 mil thick required only 14 cyclic foldings before losing its tear strength. The DSC glass transition temperature was 94° C.

EXAMPLE 10

Into a 1-liter stainless steel reactor equipped with a stirrer, nitrogen gas inlet port, and a condenser, the following were added:

291.3 g dimethyl terephthalate (DMT)

76.1 g bis(4-β-hydroxyethoxyphenyl) sulfone

218.6 g ethylene glycol

0.0919 g Mn (OAc)₂.4H₂ O

The reaction mixture was heated, under nitrogen atmosphere, at 190° C. for 4 hours. Methanol was continuously distilled out during this period. Then the following compounds were added to the reaction mixture in the reactor:

0.1093 g Sb₂ O₃

0.09309 g triphenyl phosphite

0.1788 g tetrakis [2,4-di-tertiarybutylphenyl] 4,4'-biphenylenediphosphonite

0.6127 g Pentaerythritol (PE) (0.3 mol percent based on DMT)

The reaction temperature was increased to 250° C. After 1 hour, the nitrogen gas flow was stopped, and the reaction was continued at 275° C. under 0.35 mm Hg vacuum for 4 hours. The inherent viscosity of the copolyester was 0.72. The polymer melt had fair melt strength as shown in FIG. 2. A pressed film of about 10 mil thick required 11 cyclic foldings before losing its tear strength completely. The copolyester had a Tg of 98° C., oxygen permeability of 8.4 cc.mil/100 in².day.atm., CO₂ permeability of 61.2 cc.mil/100 in².day.atm. and a melting point of 210° C.

EXAMPLE 11

(This example is a repeat of Example 2 in U.S. Pat. No. 3,558,557 using ethoxylated Bisphenol A, 10% mol ethoxylated Bisphenol A).

Using the same apparatus used in Example 7, the following were added:

291.3 g dimethyl terephthalate

232.8 g ethylene glycol

47.5 g ethoxylated Bisphenol A

0.4078 g pentaerythritol (0.199 mol % of DMT)

0.0919 g Mn (OAc)₂.4H₂ O

The reaction mixture was heated at 190° C. for 2 hours under N₂ atmosphere. Methanol was continuously distilled off during this period. Then the following compounds were added to the mixture in the reactor:

0.1093 g Sb₂ O₃

0.225 g triphenyl phosphite

0.0894 g tetrakis [2,4-di-tertiarybutylphenyl] 4,4'-biphenylenediphosphonite

The reaction temperature was increased to 260° C. and maintained for 50 minutes under N₂ atmosphere. Then the N₂ gas flow was stopped and a vacuum of less than 0.4 mm Hg was applied. The reaction was continued at 270° C. for 3 hours, 50 minutes, under vacuum. The copolyester had an inherent viscosity of 0.69. A pressed film about 10 mil thick required 52 cyclic foldings before losing its tear strength completely. The melting point was 225° C. and Tg was 76° C. The O₂ and CO₂ gas permeabilities were 10.6 and 65.2 cc.mil/100 in².day.atm., respectively. The polymer had good melt strength.

EXAMPLE 12

Poly(ethylene terephthalate) was prepared as follows:

Into a 500 ml 3-necked round bottom flask, equipped with a nitrogen gas inlet tube, stirrer and a condenser, the following compounds were added:

46.5 g dimethyl terephthalate

35.4 g ethylene glycol

0.0263 g zinc acetate dihydrate

0.01398 g antimony trioxide

The contents of the flask was heated at 220° C. under nitrogen atmosphere for 3 hours. During this time, methanol was distilled off. Then the reaction temperature was raised to 280° C., nitrogen flow was stopped and vacuum was gradually applied until less than 0.5 mm Hg. Excess ethylene glycol was continuously distilled off. The reaction was stopped after 4 hours. The inherent viscosity was 0.83, the glass transition temperature was 72° C., the oxygen permeability was 8.5 cc.mil/100 in².day.atm. and the carbon dioxide permeability was 55.3 cc.mil/100 in².day.atm. The product had very poor melt strength and had a melting point of 252° C.

Reference is made to U.S. Pat. No. 3,558,557, issued Jan. 26, 1971. From the broad disclosures of this patent it would be possible to pick the combination of the four reactants of the present invention. However, this patent is directed toward making polyesters especially for fiber application, and properties pertinent to such application are emphasized.

Moreover, one would not know to pick the particular trifunctional compound or the combination of the specific four reactants here disclosed in the amounts here disclosed to obtain the properties here set forth. For instance, column 2 equates pentaerythritol with any aromatic tri- or tetracarboxylic acid or any aliphatic alcohol having 3 or 4 hydroxyl groups. As shown herein pentaerythritol will not give the combination of properties sought in that the folding endurance is unsatisfactory. See Example 10. Nor is Example 10 itself suggested, i.e., there is no suggestion in this patent that terephthalic acid and ethylene glycol be polymerized specifically with BSE and pentaerythritol. When one substantially repeats Example 2 of the patent (as in Example 11 herein) it is noted that in this example, which uses bis-phenol-A-diglycol ether instead of BSE, the oxygen and the carbon dioxide permeabilities are entirely unsatisfactory.

Other prior art in the general field is to be found in column 1 of my U.S. Pat. No. 4,110,315, dated December 1, 1978, but none of these references disclose or suggest the compositions or the process of the present invention.

As will be evident to those skilled in the art, various modifications of this invention can be made or followed in the light of the foregoing disclosure and discussion without departing from the spirit and scope of the disclosure or from the scope of the claims. 

I claim:
 1. A thermoplastic copolyester consisting essentially of the polymeric reaction of:(A) reactant(s) selected from terephthalic acid and its C₁ to C₄ alkyl esters, and (B) reactants, bis (4-beta-hydroxyethoxyphenyl) sulfone and ethylene glycol, and (C) reactant(s) selected from (a) a triol of the formula RC(CH₂ OH)₃ where R is methyl or ethyl and (b) trimesic acid, its anhydride, and its C₁ to C₄ alkyl esters,wherein the amount of said bis (4-beta-hydroxyethoxyphenyl) sulfone is 2-25 mol percent of the amount A of reactant(s), the combined amount of B reactants is about 110 to 300 mol percent of the amount of A reactant(s), and the amount of C reactant(s) is 0.1 to 0.7 mol percent of said A reactants, said copolyester having oxygen (O₂) and CO₂ permeabilities in cc.mil/100 in.².day.atm. of less than 9 and less than 62, respectively, a glass transistion temperature, Tg, of at least 82° on an unoriented basis, said copolyester further having non-Newtonian flow properties.
 2. A copolyester of claim 1 wherein the amount of said bis (4-beta-hydroxyethoxyphenyl) sulfone is 2-20 mol percent of the amount of A reactant(s).
 3. A copolyester of claim 1 wherein (a) is selected.
 4. A copolyester of claim 3 wherein R is methyl.
 5. A copolyester of claim 3 wherein R is ethyl.
 6. A copolyester of claim 1 wherein (b) is selected.
 7. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 1. 8. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 2. 9. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 3. 10. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 4. 11. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 5. 12. In the method of forming hollow articles from a polyester made from terephthalic acid or its lower esters and one or more dioles by making a hollow preform and enclosing said preform in a softened temperature condition in a blow mold and thereafter blow molding said preform into conformance with said mold walls, the improvement comprising forming said hollow preform as a tubular shape by free extrusion of a copolyester of claim
 6. 